Prosiding Global Accepted: Effect of sintering temperature on the microstructure, electrical and magnetic properties of Zn0.98 Mn0.02O material

 
 
Penulis: Candra Kurniawan S.Si.,Prof. Drs. Perdamean Sebayang M.Sc.,Prof. Dr. Masno Ginting M.Sc.,Dr. Toto Sudiro , Didik Aryanto , S. F. Hulu
Zn 0.98 Mn 0.02 O material was synthesized from ZnO and MnO 2 powders using solid state reaction method. The microstructure, electrical and magnetic properties of Zn 0.98 Mn 0.02 O were studied as a function of sintering temperature. The X-ray diffraction analysis indicates that the main phase of synthesized sample is composed of hexagonal wurtzite ZnO phase. While the secondary phase of ZnMnO 3 were found at the sintering temperature of 700°C and 900°C. The electrical properties measurement of Zn 0.98 Mn 0.02 O sample revealed that the resistivity and the dielectric constant of samples increase with the increase of sintering temperature. The ferromagnetic properties at room temperature were observed in the Zn 0.98 Mn 0.02 O samples sintered at 500°C and 700°C. It also found that the increase in sintering temperature leads to a tendency toward the changes in the magnetic properties into paramagnetic. The presence of ZnMnO 3 secondary phases in Zn 0.98 Mn 0.02 O system is believed to be a factor that affects the decrease of the electrical and magnetic properties of the sample.

IOP Conf. Series: Materials Science and Engineering 309 (2018) 012119

ISSN / ISBN / IBSN : 1757-899X

DOI: 10.1088/1757-899X/309/1/012119

No. Arsip : LIPI-20180712
Download Disini